Nikel paduan Elektroda manual ENiCrFe-9 Pembuatan las
KOMPONEN KIMIA:
PADUAN (berat%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
ATURAN GB/T | 0,15 | 1.0-4.5 | 0,80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0,50 | 0,5-3,0 | |
ATURAN AWS | 0,15 | 1.0-4.5 | 0,75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0,50 | 0,5-3,0 | |
NILAI CONTOH | 0,07 | 2.6 | 0,28 | 4.03 | 14.3 | 66.6 | 4.41 | 0,060 | 1.67 |
PROPERTI MEKANIK:
PROPERTI | KEKUATAN HASIL (MPa) | KEKUATAN EKSTENSI (MPa) | NILAI IMAPACT J/℃ | PEMANJANGAN(%) | ||||
ATURAN GB/T | 360 | 650 | - | 18 | ||||
ATURAN AWS | - | 650 | - | 25 | ||||
NILAI CONTOH | 460 | 680 | - | 41.5 |
PARAMETER PENGELASAN YANG DIREKOMENDASIKAN:
SPESIFIKASI DIAMETER (mm) | 2,6*300 | 3.2*350 | 4.0*350 | ||||||||
LISTRIK (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
M/M | 55-80 | 65-110 | 80-130 |
Elektroda tangan tipe hidrogen rendah, komposisi nominal (persen berat) adalah Ni14Cr4FeNbMo, elektroda paduan nikel - kromium - besi.
Busur stabil, bentuk indah, percikan kecil, pembuangan terak mudah.
Ketahanan porositas yang baik, sifat mekanik logam cair stabil.
-
Nanjing Chengzhi Yongqing Energy 07MnNiMoDR tangki bola baja etilena
Internal reaktor
-
Proyek LNG-2 Arktik
KOMPONEN KIMIA:
PADUAN (berat%) | C | Mn | Si | Fe | Cr | Ni | Mo | Cu | Nb+Ta | |
ATURAN GB/T | 0,15 | 1.0-4.5 | 0,80 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0,50 | 0,5-3,0 | |
ATURAN AWS | 0,15 | 1.0-4.5 | 0,75 | 12.00 | 12.0-17.0 | ≥55 | 2.5-5.5 | 0,50 | 0,5-3,0 | |
NILAI CONTOH | 0,07 | 2.6 | 0,28 | 4.03 | 14.3 | 66.6 | 4.41 | 0,060 | 1.67 |
PROPERTI MEKANIK:
PROPERTI | KEKUATAN HASIL (MPa) | KEKUATAN EKSTENSI (MPa) | NILAI IMAPACT J/℃ | PEMANJANGAN(%) | ||||
ATURAN GB/T | 360 | 650 | - | 18 | ||||
ATURAN AWS | - | 650 | - | 25 | ||||
NILAI CONTOH | 460 | 680 | - | 41.5 |
PARAMETER PENGELASAN YANG DIREKOMENDASIKAN:
SPESIFIKASI DIAMETER (mm) | 2,6*300 | 3.2*350 | 4.0*350 | ||||||||
LISTRIK (Amp) | H/W | 69-95 | 70-115 | 95-145 | |||||||
M/M | 55-80 | 65-110 | 80-130 |